Ferpol 100 BSX15 DCPD -Laminates-

HAND CONTACT MOLDING

Once the mold is prepared, with the totally smooth surface, 3 or 4 hands of release wax are applied. On this surface is applied by means of a gun or by hand with a sponge a thin layer of V-8130.

Then a gel-coat is applied to brush or gun forming a layer of uniform thickness of 1/2mm. To proceed with the lamination the gel-coat layer must have a solid consistency but somewhat sticky to the touch.

Once the reinforcement material is prepared, the resin is prepared according to the following percentage formulation by weight;

-POLYESTER RESIN 100BXS15....... 100

-PIGMENTS...................................... 0-3

-CATALYST F11............................................. 1,5 - 2,0

100gr test of Ferpol 100BSX15 at 20ºC

REPAIR OF BREAKAGES

To repair damage to bumpers, underbody, motorcycle fairings, swimming pools or any other pieces of reinforced polyester you must follow the following steps;

-Sanding of the damaged part until the reinforcement layers are exposed.

-Perform a stratrified using the same glass reinforcements disappeared without exceeding the upper level of the break.

-Finish with a TopCoat so that later we can sand and polish the repair.

-For breaks with perforation, a plate or waxed cardboard with a smooth surface must be placed on the outside on which the missing stratified will be built.

COUNCILS

Always use in ventilated places.

To carry out a stratification it is advisable to have on hand a container with Solvent Ac1 to clean the utensils used before the hardening of the resin.

Add the pigment to all the resin that we are going to use to obtain a homogeneous color.

Prepare the fiberglass by cutting it with paper templates before starting the work.

Have a container on hand to make small mixtures of resin and catalyst to prevent it from hardening before you can use it, do not mix more than you can use.

Composition of the 1 Kg Kit:

1Kg of Ferpol 100 BSX15

25gr of F-11 Catalyst

Composition of the 5 Kg Kit:

5Kg of Ferpol 100 BSX15

100gr of Catalyst F-11

Composition of the 25 Kg Kit:

25Kg of Ferpol 100 BSX15

500gr of Catalyst F-11

Both the temperature and the amount used influence the drying process, so the data we provide are indicative.

We recommend you watch this video in which Juan Villa explains how to use resin to repair a pool: